CALCIUM
CARBONATE - SPECIFICATION |
| |
|
|
GRADES/PROPERTIES |
CALCIUM
CARBONATE - 106 |
|
Applications |
Ink |
|
Appearance |
White Powder |
|
Specific gravity (g/cm3) |
2,7 |
|
Mean
particle size(nm) |
50 |
|
BET
surface area (m2/g) |
20 min |
|
Brightness (%) |
92 min |
|
Particle shape |
Cubic |
|
Oil
absorpion (DOP) (ml/100 g) |
25 - 40 |
|
CaCO3
(%) |
98 min |
|
pH |
8,0 - 10,0 |
|
Moisture (%) |
0,5 max |
|
Degree of activity (%) |
99 min |
|
Surface coating agent |
Rosin acid |
| |
|
|
GRADES/PROPERTIES |
CALCIUM
CARBONATE - 100 |
|
Applications |
Paper |
|
Appearance |
Wet cake |
|
Specific gravity (g/cm3) |
2,7 |
|
Mean
particle size(nm) |
50 |
|
BET
surface area (m2/g) |
20 min |
|
Brightness (%) |
92 min |
|
Particle shape |
Cubic |
|
Oil
absorpion (DOP) (ml/100 g) |
- |
|
CaCO3
(%) |
98 min |
|
pH |
8,5 - 10,0 |
|
Moisture (%) |
50 max |
|
Degree of activity (%) |
- |
|
Surface coating agent |
Dispersant |
| |
|
|
GRADES/PROPERTIES |
CALCIUM
CARBONATE - 112 |
|
Applications |
Later
Products, Latex Paint |
|
Appearance |
White slurry |
|
Specific gravity (g/cm3) |
2,7 |
|
Mean
particle size(nm) |
50 |
|
BET
surface area (m2/g) |
20 min |
|
Brightness (%) |
92 min |
|
Particle shape |
Cubic |
|
Oil
absorpion (DOP) (ml/100 g) |
- |
|
CaCO3
(%) |
98 min |
|
pH |
8,0 - 10,0 |
|
Moisture (%) |
50 max |
|
Degree of activity (%) |
- |
|
Surface coating agent |
Dispersant |
| |
|
|
GRADES/PROPERTIES |
CALCIUM
CARBONATE - 201 |
|
Applications |
Rubber
product, Sealant, Adhesive |
|
Appearance |
White powder |
|
Specific gravity (g/cm3) |
2,7 |
|
Mean
particle size(nm) |
50 |
|
BET
surface area (m2/g) |
20 min |
|
Brightness (%) |
92 min |
|
Particle shape |
Cubic |
|
Oil
absorpion (DOP) (ml/100 g) |
25 - 40 |
|
CaCO3
(%) |
98 min |
|
pH |
8,5 - 10,0 |
|
Moisture (%) |
0,5 max |
|
Degree of activity (%) |
99 min |
|
Surface coating agent |
Stearic acid |
| |
|
|
GRADES/PROPERTIES |
CALCIUM
CARBONATE - 206 |
|
Applications |
Seaslant,
Adhesive, Oil paint |
|
Appearance |
White powder |
|
Specific gravity (g/cm3) |
2,7 |
|
Mean
particle size(nm) |
50 |
|
BET
surface area (m2/g) |
20 min |
|
Brightness (%) |
92 min |
|
Particle shape |
Cubic |
|
Oil
absorpion (DOP) (ml/100 g) |
25 - 40 |
|
CaCO3
(%) |
98 min |
|
pH |
8,0 - 9,5 |
|
Moisture (%) |
0,5 max |
|
Degree of activity (%) |
99 min |
|
Surface coating agent |
Fatty acid |
| |
|
|
GRADES/PROPERTIES |
CALCIUM
CARBONATE - 601 |
|
Applications |
Plastic
(PVC, PE,PP) |
|
Appearance |
White powder |
|
Specific gravity (g/cm3) |
2,7 |
|
Mean
particle size(nm) |
50 |
|
BET
surface area (m2/g) |
20 min |
|
Brightness (%) |
92 min |
|
Particle shape |
Cubic |
|
Oil
absorpion (DOP) (ml/100 g) |
25 - 40 |
|
CaCO3
(%) |
98 min |
|
pH |
8,0 - 10,5 |
|
Moisture (%) |
0,5 max |
|
Degree of activity (%) |
99 min |
|
Surface coating agent |
Coupling agent |
| |
|
|
GRADES/PROPERTIES |
CALCIUM
CARBONATE - 602 |
|
Applications |
Rubber tire,
Nitrile inner tube, Cycle tire |
|
Appearance |
White powder |
|
Specific gravity (g/cm3) |
2,7 |
|
Mean
particle size(nm) |
50 |
|
BET
surface area (m2/g) |
20 min |
|
Brightness (%) |
92 min |
|
Particle shape |
Cubic |
|
Oil
absorpion (DOP) (ml/100 g) |
25 - 40 |
|
CaCO3
(%) |
98 min |
|
pH |
8,0 - 10,5 |
|
Moisture (%) |
0,5 max |
|
Degree of activity (%) |
99 min |
|
Surface coating agent |
Coupling agent |
|